PLASTI-SOL ARMOR - WHITE (80 - 90% GLOSS)
This is a rubberized coating, with the look and feel of glossy rubber.
PLASTI-SOL ARMOR is a multi-purpose thermoplastic powder coating that utilizes polyethylene copolymer chemistry to meet and exceed a wide range of performance attributes including ultra high adhesion, impact and corrosion resistance, ultra violet (UV) protection, and graffiti resistance.
PLASTI-SOL ARMOR thermoplastic powder coatings contain no phthalates and heavy metal compliant, making PLASTI-SOL ARMOR the best choice for exceptional performance and environmental safety.
PLASTI-SOL ARMOR is an ideal choice when an all-purpose, high performance coating, with exceptional aesthetics is required. The abrasion, impact, and corrosion resistance is unsurpassed, with over 2000 hours of salt spray testing. Outdoor furniture, fencing, trailer frames, helmet facemasks, and bike racks are just a few of the typical applications that can benefit from the superior protection and durability of PLASTI-SOL ARMOR thermoplastic powder coatings.
The PLASTI-SOL ARMOR family includes several products formulated to meet a range of finishing and protection needs. Both fluid bed dip and spray grade products are available.
ADVANTAGES
• Immediate cure time • UV protected • excellent durability and chemical resistance
POWDER PROPERTIES
Cure Time - (Powder is cured until desired flow out)
PLASTI-SOL ARMOR can be applied via electrostatic deposition with or without pre-heat.
When not using pre-heat, the powder should be applied to achieve a thickness of 8 – 10mils (203 - 254µm).
Recommended voltage setting when using Corona equipment is 40 – 60 kv.
Post-baking at 350 - 425°F (175 - 220°C) for 5 to 10 minutes depending on metal thickness, or until desired flow out is achieved.
For preheated parts, the recommended preheat temperature is 400°F (205°C).
And recommended Mil thickness for is PLASTI-SOL ARMOR® 8-12mils (203 – 300µm) or higher if desired.
For improved surface finish, parts may be post-baked for a short period of time if necessary. Times and temperatures in the oven will depend on configuration and thickness of the part.
Thermoplastic powder coatings need only be heated enough to flow out the coating, nothing more.
Coverage (100% efficiency) 25.65 ft² per pound @ 8mils (5.24 m² per kg @ 203µm)
VOC Content ZERO
Thickness (Recommended) 8 – 10mils (203 – 254µm)
PERFORMANCE PROPERTIES
Melting Point 221°F (105°C)
Specific Gravity ASTM D 792 0.9414g/cm3
Adhesion ASTM D 4541 >1,000psi (7MPa)
Hardness Shore D ASTM D 2240 55
Impact Resistance ASTM B 2794 >384 in-lbs. (43 Joules)
Softening Point ASTM D 1525 162°F (72°C)
Tensile Strength ASTM D 638 3482psi (24MPa)
Elongation (%) ASTM D 638 498%
Humidity Resistance ASTM D 2247 No blistering or loss of gloss after 1000 hours
Salt Spray ASTM B 117 2,000 hrs. No significant change in color or gloss
QUV ASTM G 53 2,000 hrs. No significant change in color or gloss
Taber Abrasion ASTM D 4060 70-90mg loss, CS 17 wheel, 100mg loss, CS 17 wheel
Flexibility (Conical Mandrel Bend) ASTM D 522 1/8in (3.2mm), no cracks (>32%)
Gloss ASTM D 523 90% (Depending on color choice)
Melt Index ASTM D 1238 20